Effect of sonic treatment on the permeation performance of cellulose acetate membranes modified by n-SiO_2

Authors

GÜLSEN ASMAN
MÜRVET KAYA
NURSEL PEKEL BAYRAMGİL

DOI

10.3906/kim-1409-5

Abstract

Cellulose acetate (CA) membranes were modified by nano-silicon dioxide (n-SiO_2), and they were exposed to ultrasonic waves at a frequency of 35 kHz. The effect of sonication on their water sorption tendency and permeation capability was investigated. The characterization of the membranes was done by FTIR and SEM analysis, and the hydrophilic character of the membranes was deduced by swelling studies and contact angle (CAn) measurements. Permeation studies of the membranes were performed by using the diffusion method and theophylline was used as a model chemical in the permeation studies. The results indicated that beside the high hygroscopic property of n-SiO_2, the presence of n-SiO_2 in CA membranes did not significantly improve their hydrophilicity; however, when they were exposed to sonic waves, it was determined that the sonication effectively enhanced their water sorption capacity and permeability.

Keywords

Ultrasonic wave, cellulose acetate, membrane, nano-filler, theophylline

First Page

297

Last Page

305

Recommended Citation

ASMAN, GÜLSEN; KAYA, MÜRVET; and BAYRAMGİL, NURSEL PEKEL (2015) "Effect of sonic treatment on the permeation performance of cellulose acetate membranes modified by n-SiO_2," Turkish Journal of Chemistry: Vol. 39: No. 2, Article 9. https://doi.org/10.3906/kim-1409-5
Available at: https://journals.tubitak.gov.tr/chem/vol39/iss2/9